Pengaruh jenis Filler dan Fraksi Volume Terhadap Kekuatan Geser Sambungan Aluminium Secara Perekatan
| Main Author: | H. Setiawan, H. Setiawan |
|---|---|
| Format: | Thesis NonPeerReviewed Book |
| Bahasa: | eng |
| Terbitan: |
, 2018
|
| Subjects: | |
| Online Access: |
http://eprints.unram.ac.id/6372/1/Jurnal%20-Pengaruh%20jenis%20Filler%20dan%20Fraksi%20Volume%20Terhadap%20Kekuatan%20Geser%20Sambungan%20Aluminium%20Secar.pdf http://eprints.unram.ac.id/6372/ |
| ctrlnum |
6372 |
|---|---|
| fullrecord |
<?xml version="1.0"?>
<dc schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd"><relation>http://eprints.unram.ac.id/6372/</relation><title>Pengaruh jenis Filler dan Fraksi Volume Terhadap Kekuatan Geser 
Sambungan Aluminium Secara Perekatan</title><creator>H. Setiawan, H. Setiawan</creator><subject>T Technology (General)</subject><description>Filler is a material generally mixed in epoxy adhesives to 
change the adhesive properties especially the viscosity and to a 
certain extent can increase the stickiness of adhesion. This study 
aims to determine the effect of type and volume fraction of filler 
on epoxy adhesive to shear strength and failure modes on 
aluminum joint with epoxy adhesive. 
The joint on the made of 1100 aluminum with epoxy as 
adhesive. Filler used was fly ash, pumice stone, CaCO3, ground 
glass, and cement with the size less than 200 mesh and the 
variation of volume fraction that is 0%, 5%, 15%, and 25%. The 
specimen was glued for 24 hours, after which the shear testing 
and SEM observations were performed. 
The test results show that the shear strength value of 
aluminum joint with epoxy adhesive reaches the optimum value 
at 15% volume fraction for the five filler types. The fly ash filler 
has the highest shear strength at a 15% volume fraction of 14.10 
MPa. Overall, as seen from the mode of failure at 0%, 5%, and 
25% of the mode of failure fraction occurs in a mixture of 
interfacial and cohesive near the interface. While at the volume 
fraction of 15% failure occurs interfacially and there is also a tear 
in the adhesive. This suggests that the failure surface can be a 
clue about how well the joint strength is.</description><date>2018</date><type>Thesis:Thesis</type><type>PeerReview:NonPeerReviewed</type><type>Book:Book</type><language>eng</language><identifier>http://eprints.unram.ac.id/6372/1/Jurnal%20-Pengaruh%20jenis%20Filler%20dan%20Fraksi%20Volume%20Terhadap%20Kekuatan%20Geser%20Sambungan%20Aluminium%20Secar.pdf</identifier><identifier> H. Setiawan, H. Setiawan (2018) Pengaruh jenis Filler dan Fraksi Volume Terhadap Kekuatan Geser Sambungan Aluminium Secara Perekatan. S1 thesis, Universitas Mataram. </identifier><recordID>6372</recordID></dc>
|
| language |
eng |
| format |
Thesis:Thesis Thesis PeerReview:NonPeerReviewed PeerReview Book:Book Book |
| author |
H. Setiawan, H. Setiawan |
| title |
Pengaruh jenis Filler dan Fraksi Volume Terhadap Kekuatan Geser
Sambungan Aluminium Secara Perekatan |
| publishDate |
2018 |
| topic |
T Technology (General) |
| url |
http://eprints.unram.ac.id/6372/1/Jurnal%20-Pengaruh%20jenis%20Filler%20dan%20Fraksi%20Volume%20Terhadap%20Kekuatan%20Geser%20Sambungan%20Aluminium%20Secar.pdf http://eprints.unram.ac.id/6372/ |
| contents |
Filler is a material generally mixed in epoxy adhesives to
change the adhesive properties especially the viscosity and to a
certain extent can increase the stickiness of adhesion. This study
aims to determine the effect of type and volume fraction of filler
on epoxy adhesive to shear strength and failure modes on
aluminum joint with epoxy adhesive.
The joint on the made of 1100 aluminum with epoxy as
adhesive. Filler used was fly ash, pumice stone, CaCO3, ground
glass, and cement with the size less than 200 mesh and the
variation of volume fraction that is 0%, 5%, 15%, and 25%. The
specimen was glued for 24 hours, after which the shear testing
and SEM observations were performed.
The test results show that the shear strength value of
aluminum joint with epoxy adhesive reaches the optimum value
at 15% volume fraction for the five filler types. The fly ash filler
has the highest shear strength at a 15% volume fraction of 14.10
MPa. Overall, as seen from the mode of failure at 0%, 5%, and
25% of the mode of failure fraction occurs in a mixture of
interfacial and cohesive near the interface. While at the volume
fraction of 15% failure occurs interfacially and there is also a tear
in the adhesive. This suggests that the failure surface can be a
clue about how well the joint strength is. |
| id |
IOS5428.6372 |
| institution |
Universitas Mataram |
| institution_id |
133 |
| institution_type |
library:university library |
| library |
Perpustakaan Universitas Mataram |
| library_id |
541 |
| collection |
Institutional Repository |
| repository_id |
5428 |
| subject_area |
Law/Ilmu Hukum Scientist/Ahli Sains, Ilmuwan Agriculture/Industri Pertanian Economic Institutions/Institusi Ekonomi |
| city |
KOTA MATARAM |
| province |
NUSA TENGGARA BARAT |
| repoId |
IOS5428 |
| first_indexed |
2018-08-02T01:21:51Z |
| last_indexed |
2018-08-02T01:21:51Z |
| recordtype |
dc |
| _version_ |
1686351106382233600 |
| score |
17.538404 |