Studi mechanical properties dan struktur mikro hasil variasi temperatur dan waktu aging pada alumunium matrix composite (AMC) hasil proses stir casting dengan kandungan matrix Berlebih
| Main Author: | Saefuloh, Imam |
|---|---|
| Format: | Article info application/pdf eJournal |
| Bahasa: | eng |
| Terbitan: |
Universitas Nusantara PGRI Kediri
, 2019
|
| Online Access: |
http://ojs.unpkediri.ac.id/index.php/JMN/article/view/13503 http://ojs.unpkediri.ac.id/index.php/JMN/article/view/13503/1259 |
Daftar Isi:
- Alumunium matrix composite (AMC) banyak digunakan sebagai bahan di banyak bidang (otomotif, pertambangan, penerbangan, pertahanan) karena ringan, dipilih sebagai material ini ringan dan relatif murah dan mudah difabrikasi. Proses pembuatan AMC tidak mudah karena matrik dapat membentuk gumpalan. Proses Stir casting dipilih dalam proses ini karena dapat menghasilkan AMC lebih merata dan dapat memecah gumpalan tersebut. Setelah stir casting dilakukan proses perlakuan panas aging agar material hasil lebih baik. Penelitian ini bertujuan menggunakan alumunium sebagai matrik dan senyawa karbida SiC sebagai penguat dengan proses aging suhu 1000C dan 2000C dengan waktu penahanan selama 1, 2, 3 dan 4 jam untuk meningkatkan mechanical properties dan memperbaiki struktur mikro. Setelah melalui proses pengujian didapatkan waktu aging berpengaruh terhadap mechanical properties yang di hasilkan, semakin lama waktu aging semakin besar pula kenaikan mechanical properties, untuk nilai kekuatan tarik naik sampai 70% dan kekerasan naik sampai 31%.
- Aluminum matrix composite (AMC) is widely used as the material in many fields (automotive, mining, aviation, defense) because it is lightweight, relatively inexpensive and easily fabricated material. The process of making AMC is not easy because the matrix can form clumps. In this study, the Stir casting process was chosen because it could produce AMC more evenly and can break the clumps. After the stir casting process, the aging heat treatment process was carried out in order to produce better material. This study aimed to use aluminum as a matrix and SiC carbide compounds as reinforcement with an aging process of 1000C and 2000C with a holding time of 1, 2, 3 and 4 hours to improve mechanical properties and improve microstructures. After going through the testing process, it is found that the aging time affected the mechanical properties that were produced; the longer the aging time, the greater the mechanical properties increased, with the tensile strength value increased to 70% and the hardness increased to 31%.