PENENTUAN KAPASITANSI SPESIFIK KARBON AKTIF SEKAM PADI (Oryza sativa) HASIL MODIFIKASI DENGAN HNO3, H2SO4, DAN H2O2 DENGAN METODE CYCLIC VOLTAMMETRY
| Main Authors: | RAHMAYANTI, ZAKIR, MUHAMMAD, KARIM, ABDUL |
|---|---|
| Format: | Article |
| Bahasa: | eng |
| Terbitan: |
, 2017
|
| Subjects: | |
| Online Access: |
http://repository.unhas.ac.id/handle/123456789/24680 |
Daftar Isi:
- Sintesis dan karakterisasi karbon aktif sekam padi (Oryza sativa) hasil modifikasi dengan HNO3, H2SO4 dan H2O2 sebagai bahan elektroda superkapasitor telah dilakukan. Sekam padi telah melewati beberapa tahapan antara lain proses karbonisasi, ekstraksi silika, aktivasi dengan H3PO4, hingga modifikasi dengan HNO3, H2O2 dan H2SO4. Proses karbonisasi dilakukan pada suhu 350 oC. Hasil analisis dengan XRF menunjukkan kandungan senyawa silika pada karbon aktif sebesar 96,144 %b/b. Luas permukaan karbon aktif ditentukan dengan metode metilen biru yang menunjukkan luas permukaan karbon aktif sebesar 178,687 m2/gram. Karbon aktif hasil modifikasi dengan HNO3, H2O2, dan H2SO4 dikarakterisasi dengan metode titrasi Boehm yang ditunjang oleh FTIR. Nilai kapasitansi spesifik ditentukan dengan metode Cyclic Voltammetry pada karbon aktif termodifikasi HNO3, H2SO4, dan H2O2 berturut-turut 24,96 ??F/g, 271,812 ??F/g, dan 13,49 ??F/g. Synthesis and characterization of activated rice husks (Oryza sativa) were modified with HNO3, H2SO4 and H2O2 as supercapacitor electrode materials. Rice husk has passed several stages including carbonization process, silica extraction, activation with H3PO4, until modification with HNO3, H2O2 and H2SO4. The carbonization process was carried out at 350 oC. The results of the XRF analysis showed that the silica compound content on the activated carbon was 96.144% w/w. The surface area of activated carbon is determined by the methylene blue method which showed the surface area of activated carbon of 178,687 m2/gram. Activated carbon modified with HNO3, H2O2, and H2SO4 were characterized by Boehm titration method and supported by FTIR. Specific capacitance values were determined by Cyclic Voltammetry method on modified activated carbon HNO3, H2SO4 and H2O2 in succession 24,96 ??F/g, 271,812 ??F/g, and 13,49 ??F/g.