PHOTOCATALITIC ACTIVITY OF Fe3O4/SiO2/TiO2 COMPOSITE BY MECHANOCHEMICAL PREPARATION
| Main Authors: | S.Winatapura, Didin, Hasana Dewi, Sari, Wardiati, Siti, Fisli, Adel |
|---|---|
| Other Authors: | Center for Science and Technology of Advanced Materials-BATAN |
| Format: | Article info application/pdf eJournal |
| Bahasa: | ind |
| Terbitan: |
BATAN
, 2017
|
| Subjects: | |
| Online Access: |
http://jurnal.batan.go.id/index.php/jsmi/article/view/4015 http://jurnal.batan.go.id/index.php/jsmi/article/view/4015/3496 |
Daftar Isi:
- PHOTOCATALITIC ACTIVITY OF Fe3O4/SiO2/TiO2 COMPOSITE BY MECHANOCHEMICALPREPARATION. A simple mechanochemical activation was used to prepare Fe3O4/ SiO2/TiO2 composite. Fe3O4, and SiO2 nano particles powder were prepared by co-precipitation method respectively, while TiO2was synthesized by sol-gel method.All of the samples were mixed into vial and milled by wet milling process. The all prepared sampel were characterized by various equipments i.e. X-ray diffractometry (XRD), transmission electron microscope (TEM) and vibrating sample magnetometer (VSM), Fourier transform infrared (FTIR) and UV-Vis Spectrometer. The result shows that Fe3O4/SiO2/TiO2 composite consisted of anatase TiO2 and Fe3O4 phases. The super paramagnetic behavior of Fe3O4 nanoparticle, Fe3O4/ SiO2, and Fe3O4/SiO2/TiO2 composites exhibit the saturationmagnetic (Ms) of 89.43. and 13emu/g, respectively. The particle size of Fe3O4/SiO2/TiO2 composite was distributed in spherical shape and about 100 nm in diameter. Photocatalytic test showed that Fe3O4/SiO2/TiO2 composite can elimininate the methylene blue (MB) dye solution higher than that pure TiO2 commercial product (TiO2M) catalyst. The Fe3O4/SiO2/TiO2 composites can be easily taken back from treated water by using magnetic bar. ABSTRAK AKTIFITAS FOTOKATALITIK KOMPOSIT Fe3O4/SiO2/TiO2 DENGAN PREPARASI MECHANOCHEMICAL. Aktivasi mechanochemical sederhana digunakan untuk preparasi komposit Fe3O4/SiO2/TiO2. Serbuk nanopartikel Fe3O4 dan SiO2 masing-masing dibuat dengan metode kopresipitasi, sementara TiO2 dibuat dengan metode sol-gel. Semua sampel dicampur bersamaan di dalamvial baja tahan karat dan dihaluskan dengan proses wet milling. Sampel yang telah dibuat dikarakterisasi dengan berbagai peralatan yaitu difraksi sinar-X (XRD), mikroskop elektron transmisi (TEM), Vibrating Sample Magnetometer (VSM), Fourier Transform Infrared (FTIR) dan UV-Vis Spektrofotometer. Hasil penelitian menunjukkan bahwa Fe3O4/SiO2/TiO2 komposit terdiri dari fasa TiO2 anatase dan fasa Fe3O4. Perilaku super paramagnetic dari nano partikel Fe3O4, komposit Fe3O4/SiO2/TiO2, dan Fe3O4/SiO2/TiO2 menghasilkan saturasi magnet (Ms) berturut-turut adalah 89, 43 dan 13 emu/g. Ukuran partikel Fe3O4/SiO2/TiO2 komposit terdistribusi berbentuk speris dan berukuran diameter sekitar 100 nm. Uji fotokatalitik menunjukkan bahwa komposit Fe3O4/SiO2/TiO2 dapat menghancurkan larutan pewarna metilen biru (MB) lebih tinggi dari pada dengan katalis TiO2 murni (TiO2M) dari produk komersial dan komposit Fe3O4/SiO2/TiO2 dapat dengan mudah diambil kembali dari air yang diolah menggunakan magnet eksternal.