SINTESIS HIDROGEL KOPOLIMER PATI ILES-ILES DENGAN ASAM AKRILAT, AKRILAMIDA DAN METILENABISAKRILAMIDA SEBAGAI PEMBENAH TANAH
| Main Authors: | Sjaifullah, Achmad, Winarso, Sugeng, Budi Santoso, Agung |
|---|---|
| Other Authors: | Jurusan Kimia FMIPA - Universitas Jember |
| Format: | Article info application/pdf eJournal |
| Bahasa: | ind |
| Terbitan: |
BATAN
, 2015
|
| Subjects: | |
| Online Access: |
http://jurnal.batan.go.id/index.php/jsmi/article/view/4007 http://jurnal.batan.go.id/index.php/jsmi/article/view/4007/3478 |
Daftar Isi:
- SINTESIS HIDROGEL KOPOLIMER PATI ILES-ILES DENGAN ASAM AKRILAT, AKRILAMIDA DAN METILENABISAKRILAMIDA SEBAGAI PEMBENAH TANAH. Hidrogel kopolimer cangkok pati iles-iles dengan asam akrilat, akrilamida dan metilena bis-akrilamida disintesis menggunakan teknik polimerisasi dalam larutan dengan pelarut air dan inisiator kaliumpersulfat. Pati iles-iles yang digunakan diperoleh dengan menghomogenkan umbi iles-iles, mencucinya dengan air dan menggumpalkannya dengan metanol beberapa kali.Kelarutan pati iles-iles yang diperoleh dengan cara tersebutmencapai 5%b/b. Polimerisasi dalam larutan dilakukan tanpa hembusan gas nitrogen. Hidrogel yang dihasilkan ditentukan daya serap airnya dan struktur kimianya berdasarkan spektrum FTIR. Berdasarkan berat hidrogel yang dihasilkan dapat dikatakan bahwa sintesis menghasilkan 100 % polimerisasi pada suhu 55-60 oC. Hidrogel yang dihasilkan pada kondisi polimerisasi tertentu mempunyai daya serap air hingga 51 kali, yaitu yang disintesis dengan perbandingan konsentrasi pati iles-iles dengan asamakrilat, akrilamida dan bis-akrilamida = 1:3:3:0,01. Hidrogel kopolimer kemudian digunakan sebagai pembenah tanah dengan mempelajari kemampuan tanah berpasir dalam menyimpan dan menguapkan airnya. Tanah berpasir yang dicampur dengan 0,5 % b/b hidrogel dapat menyerap air hingga dua setengah kali dari pada tanah tanpa hidrogel dan dapat menahan lebih dari separo air yang diserapnya saat terjadi kesetimbangan penguapan dan penyerapan air. Kesetimbangan penguapan dan penyerapan air dicapai setelah 5 hari pada suhu udara 23-29 oC dan kelembaban 40-83 %. ABSTRACT SINTHESYS OF HYDROGEL COPOLYMER OF KONJAC STARCHWITHACRYLICACID, ACRYLAMIDE AND METHYLENEBISACRYLAMIDE FOR SOILAMENDMENT. Graft copolymer hydrogel of konjac starch, acrylic acid, acrylamide and N,N-methylenebisacrylamide was synthesized by techniques of polimerisation in solution with water as solvent and initiator of potassium persulfate. Konjac starches were obtained by homogenizing Konjac tuber with water and washed it with methanol several times. Konjac starch obtained with this method can produce a clear solution with up to 5 %w/w solubility. Polymerization in solution was done without nitrogen gas bubbling. The resulting hydrogel determined its water absorption and it chemical structure based on the FT-IR spectra. Based on the weight of the resulting hydrogel, the synthesis proceeds in 100 % polymerization at a temperature of 55 oC. The resulting hydrogel at certain polymerization conditions has water absorption of up to 51 times of its weight. The polymerization condition was achieved at Konjac starch concentration ratio to acrylic acid, acrylamide and N,N-methyl enebisacrylamide = 1: 3: 3: 0.01. Graft copolymer hydrogel was then used as an amendment for sandy soil to control the soil ability to store and evaporate thewater. Sandy soil mixed with 0.5 %w/whydrogel can absorb water up to two and a half times than in the absence of hydrogel and hold more than half of the water that is absorbed during the equilibrium evaporation and absorption ofwater. Equilibrium evaporation and water absorption was reached after 5 days at temperatures of 23-29 oC and humidity of 40-83 %.