STUDI PENDAHULUAN PEMBUATAN LAPISAN TIPIS MWCNT-Fe PADA PERMUKAAN GELAS DENGAN SPIN COATING
| Main Authors: | Purwanto, P., Yunasfi, Yunasfi, Mustofa, Salim |
|---|---|
| Other Authors: | Pusat Sains dan Teknologi Bahan Maju - BATAN |
| Format: | Article info application/pdf eJournal |
| Bahasa: | ind |
| Terbitan: |
BATAN
, 2015
|
| Subjects: | |
| Online Access: |
http://jurnal.batan.go.id/index.php/jsmi/article/view/4002 http://jurnal.batan.go.id/index.php/jsmi/article/view/4002/3473 |
Daftar Isi:
- STUDI PENDAHULUAN PEMBUATAN LAPISAN TIPIS MWCNT-Fe PADA PERMUKAAN GELAS DENGAN SPIN COATING. Telah dilakukan pembuatan lapisan tipis Multi-Walled Carbon Nanotubes (MWCNT)-Fe pada permukaan gelas. Pengukuran struktur kristal campuran serbuk MWCNT-Fe dilakukan dengan XRD, dimana pola difraksi yang nampak menunjukkan adanya puncak dari carbon dan Fe saja, tidak ditemukan unsur pengotor lainnya. Pengamatan morfologi dengan menggunakan SEM menunjukkan permukaan lapisan tipis MWCNT-Fe yang terbentuk pada permukaan substrat gelas. Pengukuran sifat listrik pada lapisan tipis MWCNT-Fe selanjutnya dilakukan untuk mengetahui efek perubahan frekuensi ukur terhadap nilai konduktansi dan kapasitansi. Secara umum nilai konduktansi relatif stabil terhadap perubahan frekuensi, sedangkan nilai kapasitansi lapisan tipis MWCNT-Fe mengalami penurunan seiring dengan naiknya frekuensi ukur. Namun seiring dengan bertambahnya persen (%) berat Fe di dalam lapisan tipis, nilai konduktansi lapisan tipis naik drastis, dan sebaliknya nilai kapasitansi mengalami penurunan drastis seiring dengan naiknya frekuensi pengukuran. Dari spektrum Raman terlihat adanya puncak D band pada posisi 1310 cm-1 hingga 1320 cm-1, puncak harmonik pertama G band (tangensial G band) pada posisi 1580 cm-1 hingga 1595 cm-1, dan puncak harmonik kedua G band (G’ band) pada posisi 1605 cm-1 hingga 1615 cm-1.ABSTRACT PRELIMINARY STUDY OF FABRICATION OF MWCNT-Fe THIN FILM ON GLASS BY USING SPIN COATING. The fabrication ofMWCNT-Fe thin filmon glass has been done. The measurement of crystal structure of MWCNT-Fe mixing powder has been carried out by XRD, which shows only the peak of carbon and Fe, found no other impurity elements. The observation of the surface morphology using SEM shows the surface of MWCNT-Fe thin film formed on the surface of glass substrate. The measurement of electrical properties of MWCNT-Fe thin film then was being done in order to know the effect of frequency changes against the value of conductance and capacitance against the changes of measuring frequency. In general, the conductance is relatively stable against changes in frequency, while the capacitance value of MWCNT-Fe thin film decrease with the increasing of measuring frequency. However, along with the increasing of weight percent (%) of Fe in a thin film, the conductance value of MWCNT-Fe thin film rises drastically, and contrary the value of capacitance decreased with the increasing of measuring frequency. From the Raman spectrum, it shows the D band peak at around 1310 cm-1 to 1320 cm-1, the second harmonic peak of G band (G’ band) was found at around 1605 cm-1 to 1615 cm-1, and the tangential peak of G band was found at around 1580 cm-1 to 1595 cm-1.