Karakterisasi Karbon Dari Tempurung Kemiri (Aleurites Moluccana (L) Willd) Dengan Alat XRD
| Main Authors: | Latupeirissa, Jola, Tanasale, Matheis F.J.D.P., Dade, Kalam |
|---|---|
| Format: | Article info application/pdf Journal |
| Bahasa: | eng |
| Terbitan: |
Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Pattimura
, 2017
|
| Online Access: |
https://ojs3.unpatti.ac.id/index.php/ijcr/article/view/126 https://ojs3.unpatti.ac.id/index.php/ijcr/article/view/126/100 |
Daftar Isi:
- The research of carbon characterization from candlenut shells before and after activation has been done. Activated carbon were obtained through the heating process at 350 °C for 2 hours. The carbon charcoal were further cooled and sieved with a 100 mesh sieve. Then, calcinated at 450 °C and nitrogen (N2) were flowed for 2 hours and characterized by XRD for carbon before activation. Carbon was activated by using KOH solution with a concentration of 50% for 5 hours, then dried in an oven at 120 °C for 1 hour and characterized. XRD diffractogram of crystallization for carbon before activation produced three main peak were 2.93 Å, 3.25 Å, and 8.26 Å, and at 2Ө region of 30.47°, 27.40°, and 10.70°, respectively. XRD diffractogram of crystallization for activated carbon produced three main peak were 3.0195 Å, 3.3383 Å and 8.0955 Å, the 2Ө value which was shifted of 29.560°, 26.682°, and 10.920°. This shift indicates that the distance difference between charcoal crystal face caused by KOH activator. Weight acidity solids before and after activation was 27.370 x10-3 and 33.1245x10-3 mol.g-1, respectively.