KARAKTERISTIK STRUKTUR MIKRO KOMPOSIT ASPAL SILIKA SEKAM PADI DENGAN VARIASI KOMPOSISI (20%:80%, 15%:85% dan 10%:90%)
| Main Author: | QORI SARI DEWI, 1657041001 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
, 2020
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/65937/1/ABSTRAK.pdf http://digilib.unila.ac.id/65937/2/SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/65937/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/65937/ |
Daftar Isi:
- Analisis karakteristik komposit aspal silika sekam padi dengan beberapa variasi komposisi. Bahan-bahan yang digunakan dalam penelitian ini antara lain akuades, bensin, NaOH dan HNO3. Komposit aspal silika diperoleh dari pencampuran aspal dan silika menggunakan metode padatan, yang dioven pada suhu 110°C selama 3 jam. Karakterisasi dan pengujian yang dilakukan yaitu SEM-EDS, XRD, uji kuat tarik, uji densitas dan uji porositas. Hasil karakterisasi menunjukkan permukaan komposit aspal silika terlihat adanya retakan dan gumpalan dengan ukuran rata-rata 3,483 μm, 8,127 μm, dan 7,192 μm; unsur penyusun pada sampel komposit terdiri dari unsur karbon, silikon, oksigen, sulfur, palladium dan aluminium; struktur fasa yang terbentuk pada sampel komposit terdiri dari silika amorf dan karbon amorf; nilai kuat tarik terbaik pada sampel SA1 sebesar 47,271 MPa; densitas terbaik sebesar 4,106 g/cm3 pada sampel SA3; porositas terbaik diperoleh pada SA3 sebesar 5,223%. Kata Kunci: Aspal, Silika, Sekam Padi, SEM, XRD, Kuat Tarik, Densitas dan Porositas. ABSTRACT Analysis of the characterization of rice husk and asphalt silica composites with several variation in composition. The materials used in this study include distilled water, gasoline, NaOH and HNO3. The silica asphalt composite was obtained from mixing asphalt and silica using the solids method, which is heated with a temperature of 110°C for 3 hours. Characterization and test carried out are SEM/EDS, XRD, tensile strength test, density test and porosity test. The characterization results showed that the surface of silica asphalt composites showed cracks and lumps with an average size of 3.483 μm, 8,127 μm, and 7,192 μm; the constituent elements in the composite sample consist of carbon, silicon, oxygen, sulfur, palladium and aluminum; the phase structure formed in the composite sample formed in the composite sample of amorphous silica and amorphous carbon; the best tensile strength test value in the sample SA1 wa 47,271 MPa; the best density of 4,106 g/cm3 of in the SA3 sample; the best porosity was obtained in the SA3 sampel of 5,223%. Keywords: Asphalt, Silica, Rrice Husk, SEM, XRD, Tensile Strenght, Density and Porosity.