PENGARUH PENAMBAHAN SERAT BAJA DAN SERAT POLYPROPYLENE TERHADAP KUAT TEKAN DAN KUAT LENTUR BETON
| Main Author: | NOVIA PUJA A.N., 1515011021 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS TEKNIK
, 2020
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/65170/1/ABSTRAK.pdf http://digilib.unila.ac.id/65170/3/SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/65170/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/65170/ |
Daftar Isi:
- Beton memiliki kelebihan dan kekurangan, kekurangan beton tidak dapat menahan tarik. Kekurangan ini dapat diatasi dengan menambahkan serat ke dalam beton sebagai tulangan mikro yang tersebar secara acak dalam beton. Penambahan serat bertujuan untuk meningkatkan kekuatan tarik pada beton. Pada penelitian ini, sifat mekanik yang diteliti ialah kuat tekan dan kuat lentur beton, sedangkan serat yang digunakan yaitu serat baja dan serat polypropylene. Benda uji kuat tekan berupa kubus dengan dimensi 15x15x15 cm, benda uji kuat lentur berupa balok dengan dimensi 40x10x10 cm. Variasi serat baja terdiri dari (0%; 0,5%; 1%; 1,5%) dan serat polypropylene terdiri dari (0%; 0,05%; 0,1%; 0,15%). Serat tersebut dicampurkan ke dalam beton dengan mengombinasikan serat baja dan serat polypropylene. Kuat tekan beton rencana yaitu (f’c) 25 MPa, pengujian dilakukan setelah 28 hari. Berdasarkan hasil penelitian penambahan serat baja meningkatkan kuat tekan beton pada volume fraction optimal yaitu 1% dan meningkatkan kuat lentur beton seiring bertambahnya volume fraction. Penambahan serat polypropylene meningkatkan kuat tekan beton seiring bertambahnya volume fraction dan tidak mempengaruhi kuat lentur beton. Kata Kunci: Kuat Tekan, Kuat Lentur, Serat Baja, Serat Polypropylene ABSTRACT Concrete has its excellence and weakness, the weakness of this material can’t withstand tensile stress. This weakness can be solved by adding a fiber into a concrete as micro reinforcement which is spread out randomly in concrete. The purpose addition of fiber is to enhance the flexural strength of concrete. In this research, the mechanical properties that is the compressive strength and flexural strength of concrete, the steel and polypropylene are both fibers used in this research The compressive strength specimen is cube with dimension of 15x15x15 cm, the flexural strength specimen is beams with dimension of 40x10x10 cm. The variety of steel fiber consists of (0%; 0,5%; 1%; 1,5%) and for the polypropylene fiber consists of (0%; 0,05%; 0,1%; 0,15%). These fibers are mixed into the concrete with combines steel and polypropylene fibers. The compressive strength of concrete plan is (f’c) 25 MPa , the test was held after 28 days Based on research results the addition of steel fibers enhance the concrete’s compressive strength at the volume fraction 1% and increase of the concrete’s flexural strength as the volume fraction increases. The addition of polypropylene fiber increase of the concrete’s compressive strength as the volume fraction increases, but doesn’t affect the concrete’s flexural strength. Keywords: Compressive strength, Flexural strength, Steel fiber, Polypropylene fiber.