PENGARUH VARIASI SUHU SINTERING TERHADAP PERTUMBUHAN FASE PADA SUPERKONDUKTOR BPSCCO-2212 MENGGUNAKAN METODE PENCAMPURAN BASAH
| Main Author: | M. MUNTAMIJAYATI , 1217041028 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
, 2019
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/65042/1/1.%20ABSTRAK.pdf http://digilib.unila.ac.id/65042/2/2.%20SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/65042/3/3.%20SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/65042/ |
Daftar Isi:
- Bahan superkonduktor BPSCCO-2212 dengan doping Pb = 0,2 telah disintesis dengan metode pencampuran basah. Kalsinasi dilakukan pada suhu 800 °C selama 10 jam. Sedangkan sintering dilakukan pada suhu 825 °C, 830 °C, 835 °C dan 840 °C selama 20 jam. Hasil sintesis dikarakterisasi dengan XRD (X-Ray Diffraction) dan SEM (Scanning Electron Microscopy). Hasil analisis spektrum XRD yang telah diolah menggunakan celref, menunjukkan bahwa secara umum sampel-sampel yang dihasilkan sudah membentuk fase BPSCCO-2212 (ditunjukkan adanya puncak-puncak Bi-2212) dan sudah terorientasi (ditunjukkan adanya puncak-puncak dengan h=k=0, l bilangan genap). Dari hasil perhitungan diperoleh nilai fraksi volume tertinggi pada suhu sintering 830 °C dengan nilai FV = 66,97 % dan nilai derajat orientasi tertinggi pada suhu 825 °C dengan nilai P = 76,54 %. Hasil perekam foto SEM secara umum menunjukkan bahwa kristal yang terbentuk sudah terorientasi. Kata kunci: Superkonduktor, variasi suhu sintering, penambahan Pb = 0,2 The superconducting material BPSCCO-2212 with doping Pb = 0,2 has been synthesized by the wet mixing method. Calculation is caried out at 800 °C for 10 hours. While sintering is done at 825 °C, 830 °C, 835 °C and 840 °C for 20 hours. The synthesis result were characterized by XRD X-Ray Diffraction) and SEM (Scanning Electron Microscopy). The XRD spectrum analysis results that have been processed using celref, show that in general the samples produced have formed the BPSCCO-2212 phase (indicated the presence of Bi-2212 peaks) and have been oriented (indicated the existence of peaks with h = k = 0, l even number). For the calculation result obtanced the highest volume fraction value at 830 °C sintering temperature with a value FV = 66,97 % and the highest degree of orientation at 825 °C with a value of P = 76,54 %. The results of the SEM photo recorder generally show that the crystals formed are oriented. Keywords: Superconductors, Sintering temperature variation, Addition of Pb = 0,2.