SINTESIS DAN KARAKTERISASI KALSIUM SILIKAT BERBAHAN DASAR CANGKANG (achatina fulica) BEKICOT PADA SUHU KALSINASI 1000 oC
| Main Author: | Ridho Gustiantama, 1317041038 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
, 2020
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/64947/1/ABSTRAK.pdf http://digilib.unila.ac.id/64947/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/64947/3/SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/64947/ |
Daftar Isi:
- Telah dilakukan sintesis dan karakterisasi kalsium silikat berbahan dasar cangkang bekicot (achatina fulica) pada suhu kalsinasi 1000 oC. Penelitian ini menggunakan metode reaksi padatan untuk menghasilkan kalsium silikat dari bahan CaCO3 cangkang bekicot dengan silika sekam padi. Hasil analisis DTA-TGA pada kalsium silikat cangkang bekicot memiliki puncak endotermik pada suhu 708 C dan mengalami penyusutan sebesar 27,52 %. Hasil analisis XRD kalsium cangkang bekicot memiliki fasa β-CaSiO3 sebagai fasa mayor dan α-CaSiO3 sebagai fasa minor. Hasil analisis SEM pada kalsium silikat cangkang bekicot berbentuk spheroid dengan ukuran partikel 0,246 m sampai dengan 0,925 m dan memiliki ukuran partikel rata-rata 0,448 m. Hasil analisis FTIR pada kalsium silikat cangkang bekicot memiliki gugus fungsi Si – O, Si – O – Si, Si – O – Ca, CO32-, dan O – H. Kata kunci: Kalsium silikat, CaCO3, silika, cangkang bekicot (achatina fulica), sekam padi. ABSTRACT Synthesis and characterization of calcium silicate based on snail shells (achatina fulica) has been carried out at a calcination temperature of 1000 oC. This research uses a solid reaction method to produce calcium silicate from CaCO3 material of snail shells with rice husk silica. The results of DTA-TGA analysis on snail shell calcium calcium silicate has an endothermic peak at 708 oC and experienced a shrinkage of 27.52%. The results of XRD analysis of snail shell calcium have β-CaSiO3 phase as the major phase and α-CaSiO3 as minor phase. The results of SEM analysis on calcium silicate snail-shaped spheroid shells with a particle size of 0.246 m to 0.925 m and has an average particle size of 0.448 m. The results of FTIR analysis on snail shell calcium silicate have functional groups Si - O, Si - O - Si, Si - O - Ca, CO32-, and O - H. Keywords: Calcium silicate, CaCO3, silica, snail shell (achatina fulica), rice husk.