SINTESIS DAN KARAKTERISASI ASPAL SILIKA DENGAN PERLAKUAN TERMAL
| Main Author: | Juniati Br Simbolon, 1727041004 |
|---|---|
| Format: | Masters NonPeerReviewed Book Report |
| Terbitan: |
, 2020
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/64402/1/ABSTRAK.pdf http://digilib.unila.ac.id/64402/2/TESIS%20FULL.pdf http://digilib.unila.ac.id/64402/3/TESIS%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/64402/ |
Daftar Isi:
- ABSTRAK SINTESIS DAN KARAKTERISASI ASPAL SILIKA DENGAN PERLAKUAN TERMAL Oleh JUNIATI BR SIMBOLON Penelitian dilakukan untuk mengetahui pengaruh variasi suhu termal terhadap komposit aspal silika terhadap gugus fungsi, karakteristik termal, struktur fasa, ukuran butir, porositas, densitas, serta kuat. Pembuatan komposit aspal silika dilakukan dengan menggunakan perbandingan massa aspal dan silika yaitu 1:2 dengan variasi suhu sintering sebesar 300 ̊C, 400 ̊C, dan 450 ̊C dengan waktu tahan selama 1 jam. Hasil analisis FTIR tidak adanya gugus fungsi baru terkait komposit aspal silikamengindikasikan bahwa sampel tidak bereaksi secara kimia. Hasil analisis XRD menunjukkan pada setiap sampel fasa yang terbentuk adalah fasa amorf. Karbon amorf terdeteksi pada 2Ɵ=22°. Sedangkan fasa silika amorf mengalami pergeseran pada rentang 2Ɵ= 19°-23°. Hasil analisis TGA menunjukkan bahwa penggunaan variasi suhusintering terhadap sampel mengakibatkan penyusutan massa hingga 28%. Sementara hasil analisis DTA menunjukkan bahwa sampel AS300, AS400, dan AS450 mengalami peningkatan suhu puncak endotermik. Selain itu, terjadi peningkatan suhu puncak eksotermik pada setiap sampel yang mengindikasikan bahwa ketahanan sampel terhadap penguraian panas semakin meningkat. Hasil uji fisis menunjukkan dengan penambahan paduan silika yang lebih besar dan dengan menggunakan variasi suhu sintering yang lebih tingi mengakibatkan peningkatan nilai densitas dan menurunnya nilai porositas serta kuat tekan. Kata kunci: aspal, karakteristik termal, silika sekam padi, struktur fasa, densitas, porositas ABSTRACT SYNTHESIS AND CHARACTERIZATION OF SILICA ASPHALT WITH THERMAL TREATMENT By JUNIATI BR SIMBOLON The research was conducted to determine the effect of thermal temperature variations on silica asphalt composites on functional groups, thermal characteristics, phase structure, grain size, porosity, density, and strength. The silica asphalt composite was made by using a mass ratio of asphalt and silica, namely 1: 2 with sintering temperature variations of 300 C, 400 ̊C, and 450 ̊C with a holding time of 1 hour. The results of FTIR analysis of the absence of new functional groups related to silica asphalt composites indicate that the samples did not react chemically. The XRD analysis results showed that each sample phase formed was an amorphous phase. Amorphous carbon was detected at 2Ɵ = 22 °. Meanwhile, the amorphous silica phase experienced a shift in the range of 2Ɵ = 19 ° -23 °. The results of the TGA analysis showed that the use of temperature variations of the sample resulted in mass shrinkage of up to 28%. Meanwhile, the results of the DTA analysis showed that samples AS300, AS400, and AS450 experienced an increase in endothermic peak temperatures. In addition, there was an increase in the exothermic peak temperature for each sample, indicating that the resistance of the sample to heat decomposition was increasing. The physical test results showed that the addition of a larger silica alloy and by using a higher sintering temperature variation resulted in an increase in the density value and a decrease in the value of porosity and compressive strength. Keywords: asphalt, thermal characteristics, silica of rice husk, phase structure, density, porosity