UNJUK KERJA OLIGOMER 4-VINILPIRIDIN SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM LARUTAN KOROSIF YANG MENGANDUNG KEROSIN
| Main Author: | TRIA PRABOWO , 1517011107 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
, 2020
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/62170/1/ABSTRAK.pdf http://digilib.unila.ac.id/62170/2/SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/62170/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/62170/ |
Daftar Isi:
- Pada penelitian ini, oligomer 4-vinilpiridin disintesis menggunkan inisiator hidrogen peroksida sebanyak 0,25 mol dengan metode polimerisasi. Senyawa O(4-VP) kemudian dikarakterisasi struktur dan berat molekulnya dengan spektrofotometer Fourier Transform Infra-Red (FTIR) dan spektroskopi massa. Senyawa O(4-VP) kemudian digunakan sebagai inhibitor korosi baja lunak dalam larutan korosif mengandung kerosin, dengan tujuan utama untuk menyelidiki efek dari konsentrasi dan suhu pada aktivitas inhibisi yang dinyatakan dalam bentuk laju korosi dan persen proteksi. Pengujian aktivitas O(4-VP) dilakukan dengan metode kehilangan berat (Wheel Test), Electrochemical Impedance Spectroscopy (EIS), dan Plot Tafel. Analisis permukaan dilakukan dengan Scaning Electron Microscopy (SEM). Hasil sintesis O(4-VP) berupa cairan kental berwarna orange. Spektrum massa menunjukkan bahwa senyawa O(4-VP) terdeteksi mempunyai berat molekul 100-900 m/z yang berhubungan dengan panjang rantai 1-9 unit monomer, unit monomer yang paling banyak adalah tetramer (n = 4). Spektrum FTIR menghasilkan puncak-puncak pada bilangan gelombang 2937 cm-1 menunjukkan serapan gugus C-H alifatik yang terkandung pada O(4-VP). Hasil screening test dengan metode wheel test tampak bahwa senyawa O(4-VP) efisien dalam menghambat laju korosi, dengan persen proteksi sebesar 65% pada konsentrasi 150 mg L-1. Hasil pengujian aktivasi dengan metode EIS dan Tafel menunjukkan bahwa O(4-VP) efektif pada suhu 50 oC. Penambahan konsentrasi terbaik adalah 150 mg L-1 dengan nilai persen proteksi diatas 80 %. Hasil analisis permukaan dengan SEM menunjukkan bahwa O(4-VP) mampu menurunkan laju korosi, yang dihasilkan dengan citra permukaan baja lunak pada blanko mengalami kerusakan yang lebih parah dibandingkkan dengan baja lunak yang ditambahkan O(4-VP). Kata Kunci: oligomer 4-vinilpiridin, inhibitor korosi, korosi CO2, larutan korosif, kerosin. In this study, the oligomer 4-vinylpyridine was synthesized by hydrogen peroxide 0.2 mol using polymerization method. The oligomer 4-VP was characterized in terms of molecular weight and structure by Fourier Transform Infra-Red (FTIR) spectrophotometer and mass spectroscopy. The oligomer 4-VP was tested as corrosion inhibitor for mild steel in corrosive solution containing kerosene, with the main purpose to investigate the effect of inhibitor concentrations and temperatures on the inhibition acivity defined in terms of corrosion rate and percent of protection. The oligomer 4-VP activity was carried out using the methods of Wheel Test (WT), Electrochemical Impedance Spectroscopy (EIS) and Tafel Diagram. The surface analysis was performed with Scanning Electron Microscopy (SEM). The results of O(4-VP) synthesis was condensed solution with orange colour. The mass spectrum show that the O(4-VP) compound has the molecular weight of 100-900 m/z corresponding to the length of the 1-9 monomer chains, and the prime oligomer is tetramer (n = 4). The spectrum of FTIR showed peaks at wave number 2937 cm-1 show absorption function group C-H aliphatic of the O(4-VP). The results of screening test using Wheel Test method show that the O(4-VP) compound is effective to reduce corrosion rate with a protection percentage of 65% at 150 mg L-1. The results of testing O(4-VP) activity test with the EIS and Tafel method show that O(4-VP) is efficient at temperatures 50 oC. The best concentration addition is 150 mg L-1 with protection percentage above 80 %. The results of surface analysis with SEM show that O(4-VP) can reduce the corrosion rate, which is proven by the results of surface image of blank mild steel is more severe damage compared to mild steel added O(4-VP). Keywords: oligomer 4-vinylpyridine, corrosion inhibitor, CO2 corrosion, corrosive solutions, kerosene.