ADSORPSI - DESORPSI ION Cu(II) DAN Ni(II) PADA KARBON AKTIF DARI TEMPURUNG KELAPA SAWIT YANG DIMODIFIKASI DENGAN MAGNETIT
| Main Author: | ANNISAA SITI ZULAICHA , 1727011002 |
|---|---|
| Format: | Masters NonPeerReviewed Book Report |
| Terbitan: |
, 2019
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/60291/1/ABSTRAK.pdf http://digilib.unila.ac.id/60291/2/TESIS%20FULL.pdf http://digilib.unila.ac.id/60291/3/TESIS%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/60291/ |
Daftar Isi:
- Penelitian ini bertujuan untuk mengetahui kemampuan adsorpsi karbon aktif dari tempurung kelapa sawit yang dilapisi dengan magnetit terhadap larutan ion Cu(II) dan Ni(II). Pembuatan karbon aktif fisika kimia (KAFKM) diawali dengan aktivasi karbon tempurung kelapa sawit secara fisika-kimia yaitu melalui pemanasan pada suhu 700C dan penggunaan H3PO4. Pelapisan magnetit pada karbon aktif dilakukan dengan penambahan larutan Fe3+/Fe2+ pada suspensi karbon aktif yang dilanjutkan dengan penambahan larutan NaOH hingga pH 10. Karakterisasi yang dilakukan pada KAFKM meliputi SEM-EDX, XRD, SBET, dan FT-IR. Kondisi optimum adsorpsi ion Cu(II) dan Ni(II) diperoleh pada penggunaan 0,4 dan 0,5 gram adsorben, dengan persentase adsorpsi sebesar 99,59 dan 99,11%. Kemudian volume adsorbat yaitu 25 mL pada pH optimum 5 dan 6 untuk larutan ion Cu(II) dan Ni(II) dengan waktu kontak optimum 90 menit. Kinetika adsorpsi ion logam terhadap KAFK dan KAFKM cenderung mengikuti model kinetika adsorpsi pseudo dua dan isoterm adsorpsi cenderung mengikuti pola isoterm adsorpsi Langmuir. Kata kunci: Tempurung kelapa sawit, karbon aktif magnetit, adsorpsi, ion Cu (II), ion Ni(II). ABSTRACT This study aims to determine the ability of activated carbon adsorption from palm oil shells coated with magnetite to Cu(II) and Ni(II) ion in solutions. The activated carbon with magnetit coating (KAFKM) was synthesized through several stages namely carbonization of palm oil shells, activation of physicalchemical process, and coating of magnetite on activated carbon. The physicalchemical activation was carried out by heating at 700C and continued by using H3PO4 as a chemical activator. The magnetite coating on activated carbon (KAFK) was done by adding Fe3+/Fe2+ solution to an activated carbon suspension followed by adding NaOH solution up to pH 10. Characterization performed on KAFKM included SEM-EDX, XRD, SBET, and FT-IR. The optimum conditions of adsorption of Cu(II) and Ni(II) ions were obtained at the use of 0.4 and 0.5 grams of adsorbent, with adsorption percentages of 99.59 and 99.11%. The optimum of pH was obtained at 5 and 6 for Cu(II) and Ni(II) ions respectively with 90 minutes contact time. Kinetic and isotherm adsorption of Cu(II) and Ni(II) ions on KAFK and KAFKM follow pseudo second order kinetic model and Langmuir adsorption isotherm pattern. Keywords: Palm oil shells, magnetite activated carbon, adsorption, Cu(II) ions, Ni(II) ions.