PENGARUH SUHU SINTERING TERHADAP TINGKAT KEMURNIAN FASE SUPERKONDUKTOR BPSCCO-2223 PADA KADAR Ca 2,10 MENGGUNAKAN METODE PENCAMPURAN BASAH

Main Author: RIZKI PUTRI SURAHMAN, 1417041073
Format: Bachelors NonPeerReviewed Book Report
Terbitan: UNIVERSITAS LAMPUNG , 2019
Subjects:
Q Science (General)
QC Physics
Online Access: http://digilib.unila.ac.id/55871/1/ABSTRAK.pdf
http://digilib.unila.ac.id/55871/3/SKRIPSI%20FULL.pdf
http://digilib.unila.ac.id/55871/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
http://digilib.unila.ac.id/55871/
ctrlnum 55871
fullrecord <?xml version="1.0"?> <dc schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd"><title>PENGARUH SUHU SINTERING TERHADAP TINGKAT KEMURNIAN FASE SUPERKONDUKTOR BPSCCO-2223 PADA KADAR Ca 2,10 MENGGUNAKAN METODE PENCAMPURAN BASAH</title><creator>RIZKI PUTRI SURAHMAN, 1417041073</creator><subject>Q Science (General)</subject><subject>QC Physics</subject><description>Penelitian ini dilakukan untuk mengetahui pengaruh suhu sintering terhadap tingkat kemurnian fase superkonduktor BPSCCO-2223 menggunakan metode pencampuran basah. Bahan yang digunakan yaitu Bi2O3, PbO, SrCO3, CaCO3, CuO, NHO3 dan aquades. Sintesis dilakukan dengan melarutkan bahan menggunakan HNO3 dan aquades secara perlahan. Kemudian, larutan dikeringkan selama 40 jam dengan suhu 300, 400, dan 600 &#xB0;C secara bertahap. Sampel dikalsinasi selama 10 jam pada suhu 800 &#xB0;C dan di sintering selama 20 jam dengan variasi suhu 850, 855, 860, dan 865 &#xB0;C. Hasil XRD menunjukkan kemurnian fase meningkat seiring bertambahnya suhu sintering yang ditunjukkan dengan nilai fraksi volume. Fraksi volume yang relatif besar pada sampel BPSCCO-2223-865 sebesar 87,20 %. Sementara, fraksi volume terkecil adalah BPSCCO-2223-850 sebesar 58,25%. Derajat orientasi yang relatif besar pada sampel BPSCCO-2223-855 sebesar 27,64 %. Sementara, derajat orientasi terkecil BPSCCO-2223-860 sebesar 21,16 %. Hasil SEM menunjukkan bahwa semua sampel telah memiliki lapisan-lapisan yang tersusun (terorientasi) dengan ruang kosong antara lempengan (void) relatif kecil.&#xD; &#xD; &#xD; Kata kunci: Superkonduktor, BPSCCO-2223, sintering, fraksi volume, dan derajat orientasi.&#xD; &#xD; &#xD; &#xD; ABSTRACT&#xD; &#xD; Study was conducted to determine the effect of sintering temperature on the phase purity level superconductor using the wet-mixing method. The materials used are Bi2O3, PbO, SrCO3, CaCO3, CuO, NHO3 and aquades. Synthesis carried out by slowly dissolving HNO3 and aquades then gradually for 40 hours dried out at a temperature of 300, 400, 600 &#xB0;C. The sample was analysed with calcination for 10 hours at 800 &#xB0;C and sintering for 20 hours using variations of temperature on each 850, 855, 860, and 865 &#xB0;C. The XRD results show that phase purity which increases with increasing sintering temperature which indicated by the volume fraction value. The relative high volume fraction of the BPSCCO-2223-865 sample is 87,20% while, the lowest volume fraction of BPSCCO-2223-850 is 58,25%. The relative high orientation degree of BPSCCO-2223-855 is 27,64% and the lowest orientation degree of BPSCCO-2223-860 is 21,16%. The SEM result shows that all samples have layers arranged (oriented) by empty spaces between relatively small plaque (void).&#xD; &#xD; &#xD; Key words. Superconductor, BPSCCO-22223, sintering, volume fraction, and degree of orientation.</description><publisher>UNIVERSITAS LAMPUNG</publisher><date>2019-02-06</date><type>Thesis:Bachelors</type><type>PeerReview:NonPeerReviewed</type><type>Book:Book</type><identifier>http://digilib.unila.ac.id/55871/1/ABSTRAK.pdf</identifier><type>Book:Book</type><identifier>http://digilib.unila.ac.id/55871/3/SKRIPSI%20FULL.pdf</identifier><type>Book:Book</type><identifier>http://digilib.unila.ac.id/55871/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf</identifier><identifier> RIZKI PUTRI SURAHMAN, 1417041073 (2019) PENGARUH SUHU SINTERING TERHADAP TINGKAT KEMURNIAN FASE SUPERKONDUKTOR BPSCCO-2223 PADA KADAR Ca 2,10 MENGGUNAKAN METODE PENCAMPURAN BASAH. UNIVERSITAS LAMPUNG, FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM. </identifier><relation>http://digilib.unila.ac.id/55871/</relation><recordID>55871</recordID></dc>
format Thesis:Bachelors
Thesis
PeerReview:NonPeerReviewed
PeerReview
Book:Book
Book
Report:Report
Report
author RIZKI PUTRI SURAHMAN, 1417041073
title PENGARUH SUHU SINTERING TERHADAP TINGKAT KEMURNIAN FASE SUPERKONDUKTOR BPSCCO-2223 PADA KADAR Ca 2,10 MENGGUNAKAN METODE PENCAMPURAN BASAH
publisher UNIVERSITAS LAMPUNG
publishDate 2019
isbn 9781417041077
topic Q Science (General)
QC Physics
url http://digilib.unila.ac.id/55871/1/ABSTRAK.pdf
http://digilib.unila.ac.id/55871/3/SKRIPSI%20FULL.pdf
http://digilib.unila.ac.id/55871/2/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
http://digilib.unila.ac.id/55871/
contents Penelitian ini dilakukan untuk mengetahui pengaruh suhu sintering terhadap tingkat kemurnian fase superkonduktor BPSCCO-2223 menggunakan metode pencampuran basah. Bahan yang digunakan yaitu Bi2O3, PbO, SrCO3, CaCO3, CuO, NHO3 dan aquades. Sintesis dilakukan dengan melarutkan bahan menggunakan HNO3 dan aquades secara perlahan. Kemudian, larutan dikeringkan selama 40 jam dengan suhu 300, 400, dan 600 °C secara bertahap. Sampel dikalsinasi selama 10 jam pada suhu 800 °C dan di sintering selama 20 jam dengan variasi suhu 850, 855, 860, dan 865 °C. Hasil XRD menunjukkan kemurnian fase meningkat seiring bertambahnya suhu sintering yang ditunjukkan dengan nilai fraksi volume. Fraksi volume yang relatif besar pada sampel BPSCCO-2223-865 sebesar 87,20 %. Sementara, fraksi volume terkecil adalah BPSCCO-2223-850 sebesar 58,25%. Derajat orientasi yang relatif besar pada sampel BPSCCO-2223-855 sebesar 27,64 %. Sementara, derajat orientasi terkecil BPSCCO-2223-860 sebesar 21,16 %. Hasil SEM menunjukkan bahwa semua sampel telah memiliki lapisan-lapisan yang tersusun (terorientasi) dengan ruang kosong antara lempengan (void) relatif kecil. Kata kunci: Superkonduktor, BPSCCO-2223, sintering, fraksi volume, dan derajat orientasi. ABSTRACT Study was conducted to determine the effect of sintering temperature on the phase purity level superconductor using the wet-mixing method. The materials used are Bi2O3, PbO, SrCO3, CaCO3, CuO, NHO3 and aquades. Synthesis carried out by slowly dissolving HNO3 and aquades then gradually for 40 hours dried out at a temperature of 300, 400, 600 °C. The sample was analysed with calcination for 10 hours at 800 °C and sintering for 20 hours using variations of temperature on each 850, 855, 860, and 865 °C. The XRD results show that phase purity which increases with increasing sintering temperature which indicated by the volume fraction value. The relative high volume fraction of the BPSCCO-2223-865 sample is 87,20% while, the lowest volume fraction of BPSCCO-2223-850 is 58,25%. The relative high orientation degree of BPSCCO-2223-855 is 27,64% and the lowest orientation degree of BPSCCO-2223-860 is 21,16%. The SEM result shows that all samples have layers arranged (oriented) by empty spaces between relatively small plaque (void). Key words. Superconductor, BPSCCO-22223, sintering, volume fraction, and degree of orientation.
id IOS4198.55871
institution Universitas Lampung
institution_id 43
institution_type library:university
library
library Perpustakaan Universitas Lampung
library_id 537
collection Digital Repository Unila
repository_id 4198
subject_area Miscellany of Technology and Applied Sciences/Aneka Ragam tentang Teknologi dan Ilmu Terapan
Research of Social Science/Metode Riset Penelitian Ilmu Sosial, Statistik Ilmu Sosial
Agriculture/Industri Pertanian
Econmics/Ilmu Ekonomi
city KOTA BANDAR LAMPUNG
province LAMPUNG
shared_to_ipusnas_str 1
repoId IOS4198
first_indexed 2019-05-07T03:33:40Z
last_indexed 2019-05-07T03:33:40Z
recordtype dc
_version_ 1686096934728630272
score 17.538404

Lihat Juga