SINTESIS ZEOLIT ZSM-5 DARI KALENG ALUMINIUM BEKAS DAN SILIKA SEKAM PADI SEBAGAI KATALIS TRANSESTERIFIKASI MINYAK BIJI KARET MENJADI BIODIESEL
| Main Author: | GANJAR ANDHULANGI , 1417011047 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
, 2018
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/54814/1/ABSTRAK.pdf http://digilib.unila.ac.id/54814/2/SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/54814/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/54814/ |
Daftar Isi:
- Pada penelitian ini, zeolit ZSM-5 disintesis dengan rasio molar Si/Al 10 dari kaleng aluminium bekas dan silika sekam padi menggunakan metode hidrotermal. Kristalisasi dilakukan dengan variasi waktu 24, 48, 72, dan 96 jam, dilanjutkan dengan kalsinasi pada suhu 550 °C, dan diujicobakan sebagai katalis transesterifikasi terhadap minyak biji karet. Pengaruh konversi sampel menjadi H-ZSM-5 pada aktivitas katalitik juga dipelajari. Katalis dikarakterisasi menggunakan beberapa teknik untuk mengungkapkan beberapa karakteristik fisik dari sampel. Karakterisasi menggunakan XRD mengindikasikan adanya fasa amorf yang mendominasi, oleh karena itu sampel dispesifikasikan sebagai prekursor ZSM-5. Keberadaan sampel sebagai material amorf didukung juga melalui hasil analisis SEM yang mengungkapkan heterogenitas permukaan ditunjukkan oleh berbagai ukuran dan bentuk partikel yang tersebar secara acak pada permukaan. Prekursor ZSM-5 diuji aktivitasnya sebagai katalis transesterifikasi terhadap minyak biji karet untuk mengetahui kemampuan katalitiknya dalam mengkonversi asam lemak minyak biji karet menjadi metil ester yang dapat diidentifikasi menggunakan metode GC-MS. Aktivitas katalitik ini dikaitkan dengan keberadaan situs asam Lewis dan Bronsted Lowry yang ditunjukkan oleh hasil FTIR. Kata kunci : zeolit ZSM-5, kaleng aluminium bekas, silika sekam padi, biji karet, metode transesterifikasi, biodiesel In this study, hydrothermal method was applied to synthesize ZSM-5 zeolites with the molar ratio of Si to Al (Si/Al) of 10 from waste aluminium can and rice husk silica. Crystallization was carried out at different times of 24, 48, 72, and 96 hours, followed by calcination treatment at 550 °C, and then tested as catalyst for transesterification of rubber seed oil. The effect of conversion of the sample into H-form (HZSM-5) on catalytic activity was also investigated. The catalysts were characterized using several techniques to reveal some physical characteristics of the samples. Characterization using XRD indicates the domination of amorphous phase, therefore the samples are specified as ZSM-5 precursor. The existence of the samples as amorphous material is also supported by the results of SEM analysis which reveals the heterogeneity of the surface as displayed by different sizes and shapes of the particle spread randomly on the surface. Activity test of the ZSM-5 precursor as catalyst for transesterification of rubber seed oil demonstrated the ability of the precursor to catalyze the conversion of fatty acids in rubber seed oil into their corresponding methylesters, as detected using GC-MS method. This catalytic activity is associated with the presence of Lewis and Bronsted Lowry acid sites as indicated by the FTIR results. Key words : ZSM-5 zeolites, waste aluminium can, rice husk silica, rubber seed oil, transesterification method, biodiesel