KONVERSI MINYAK JARAK PAGAR (Jatropha curcas L.) MENJADI BIODIESEL DENGAN KATALIS ZEOLIT ZSM-5 BERBAHAN DASAR SILIKA SEKAM PADI DAN ALUMINIUM KALENG BEKAS
| Main Author: | HERLIANA , 1417011053 |
|---|---|
| Format: | Bachelors NonPeerReviewed Book Report |
| Terbitan: |
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
, 2018
|
| Subjects: | |
| Online Access: |
http://digilib.unila.ac.id/54778/2/ABSTRAK.pdf http://digilib.unila.ac.id/54778/4/SKRIPSI%20FULL.pdf http://digilib.unila.ac.id/54778/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf http://digilib.unila.ac.id/54778/ |
Daftar Isi:
- Pada penelitian ini, zeolit ZSM-5 dengan nisbah Si/Al 30 telah disintesis dari silika sekam padi dan aluminium kaleng bekas dengan metode hidrotermal pada suhu 100 °C dan variasi waktu kristalisasi selama 24, 48, 72, dan 96 jam. Zeolit yang dihasilkan kemudian dikalsinasi pada suhu 550 °C selama 5 jam. Karakterisasi zeolit dengan XRD menunjukkan bahwa sampel masih dalam bentuk amorf (prekursor ZSM-5). Fasa amorf pada sampel juga didukung oleh hasil SEM yang menunjukkan bahwa sampel memiliki morfologi permukaan yang heterogen baik bentuk, ukuran, dan penyebaran pada permukaan. Analisis FTIR menunjukkan bahwa sampel mengandung situs asam Lewis dan setelah proses pertukaran ion menunjukkan adanya situs asam Brønsted-Lowry. Uji katalitik transesterifikasi minyak jarak pagar menunjukkan bahwa prekursor ZSM-5 yang disintesis memiliki unjuk kerja katalis, ditandai dengan terkonversinya asam lemak dalam minyak jarak pagar menjadi metil ester berdasarkan hasil analisis GC-MS, meskipun persen konversi yang diperoleh relative rendah (sekitar 20%). Selain itu, parameter fisik biodiesel yang meliputi densitas dan titik nyala, belum memenuhi syarat mutu SNI 7182:2015, sehingga diperlukan adanya penelitian lebih lanjut. Kata Kunci: zeolit ZSM-5, hidrotermal, Brønsted-Lowry, transesterifikasi, biodiesel. CONVERSION OF Jatropha curcas L. OIL INTO BIODIESEL WITH ZSM-5 ZEOLITE CATALYST BASE ON RICE HUSK SILICA AND WASTE ALUMINUM CANS In this study, ZSM-5 zeolite with Si/Al ratio of 30 was synthesized from rice husks silica and waste aluminum cans, using hydrothermal method at 100 °C and varied crystallization times of 24, 48, 72, and 96 hours. The zeolites produced were calcined at 550 °C for 5 hours. Characterization of zeolites with XRD shows that the samples are still in amorphous state (ZSM-5 precursor). This amorphous phase of the samples is also supported by SEM results which show the existence of heterogeneous morphology of the surface, both in terms of particle shape, size, and distribution over the surface. The FTIR analysis of representative sample contains Lewis acid site and after ion exchange revealed the presence of Brønsted-Lowry acid site. Catalytic test for transesterification of jatropha oil demonstrated that the ZSM-5 precursor synthesized exhibit the ability to catalyze the conversion of fatty acids in jatropha oil to their corresponding methyl esters, as revealed by GC-MS, although the percent conversion is relatively low (around 20%). Furthermore, the physical parameters of the biodiesel such as density and flash point are not in the values specified in the SNI 7182:2015 biodiesel, suggesting the need for further investigation. Keyword: ZSM-5 zeolite, hydrothermal, Brønsted-Lowry, transesterification, biodiesel.