SINTESIS DAN KARAKTERISASI ZEOLIT-TiO2 SERTA PEMANFAATANNYA SEBAGAI FOTOKATALIS UNTUK DEGRADASI RHODAMIN B
| Main Authors: | Fauzi, W. A., Simpen, I N., Sudiarta, I W. |
|---|---|
| Format: | Article info application/pdf eJournal |
| Bahasa: | eng |
| Terbitan: |
Program Studi Kimia, FMIPA, Universitas Udayana (Program of Study in Chemistry, Faculty of Mathematics and Natural Sciences, Udayana University), Bali, Indonesia
, 2019
|
| Online Access: |
https://ojs.unud.ac.id/index.php/jchem/article/view/45728 https://ojs.unud.ac.id/index.php/jchem/article/view/45728/27746 |
Daftar Isi:
- The synthesis of zeolite-TiO2 composite has been successfully performed by mixing the H2SO4-enriched natural zeolite to TiO2. The composites are formed then characterized functional groups using Fourier Transform Infrared (FTIR) and surface area with BET (Breunaur, Emmet and Teller) method. The characterization results showed that the synthesis of zeolite-TiO2 composites is relatively successful. Those can be seen from BET characterization higher to the composite surface area from 63.031 m2/g to 73.913 m2/g, then reinforced by the appearance of the functional groups of TiO2 in zeolite at wavelength 2345.44 cm-1, 792.74 cm-1 and 424.34 cm-1. Furthermore, the composite is used for the photodegradation of rhodamin B dyes with the highest degradation percentage was 97.39% in optimal irradiation contact time was reached at 10 minutes and the effective pH of 4
- Sintesis komposit zeolit-TiO2 telah berhasil dilakukan dengan mencampurkan zeolit alam terkativasi H2SO4 dengan TiO2. Komposit yang terbentuk kemudian dikarakterisasi gugus fungsi dengan Fourier Tranform Infrared (FTIR) dan luas permukaan secara metode BET (Breunaur, Emmet dan Teller). Hasil karakterisasi FTIR dan BET menunjukkan bahwa sintesis komposit zeolit-TiO2 relatif berhasil. Hal tersebut dapat dilihat dari karakterisasi BET, yaitu semakin tinggi luas permukaan komposit dari 63,031 m2/g menjadi 73,913 m2/g, kemudian diperkuat dengan munculnya gugus fungsi TiO2 pada zeolit pada panjang gelombang 2345,44 cm-1, 792,74 cm-1, dan 424,34 cm-1. Selanjutnya, komposit digunakan untuk fotodegradasi zat warna rhodamin B dengan persentase tertinggi 97,39% pada waktu kontak irradiasi optimum menit ke-10 dan pH efektif larutan 4.