PEMANFAATAN ZEOLIT ALAM SUMATERA BARAT SEBAGAI PENDUKUNG TiO2 DALAM DEGRADASI CONGO RED SERTA SIMULASI LIMBAH SECARA FOTOLISIS
| Main Author: | Muhammad, Lucky Fajri |
|---|---|
| Format: | Thesis NonPeerReviewed Book |
| Bahasa: | ind |
| Terbitan: |
, 2016
|
| Subjects: | |
| Online Access: |
http://scholar.unand.ac.id/17011/1/Abstrak.pdf http://scholar.unand.ac.id/17011/2/BAB%20I.%20PENDAHULUAN.pdf http://scholar.unand.ac.id/17011/3/BAB%20V.%20PENUTUP.pdf http://scholar.unand.ac.id/17011/4/DAFTAR%20PUSTAKA.pdf http://scholar.unand.ac.id/17011/5/Makalah%20full.pdf http://scholar.unand.ac.id/17011/ |
Daftar Isi:
- Zeolit Clinoptilolit-Ca telah berhasil digunakan sebagai pendukung TiO2 dalam sintesis TiO2/zeolit sebagai fotokatalis dalam mendegradasi Congo Red 20 mg/L dan simulasi limbah Congo Red dibawah sinar lampu UV 365 nm. TiO2/zeolit hasil sintesis dikarakterisasi menggunakan Fourier Transform Infra Red (FTIR) dan X-Ray Diffraction (XRD). Dari hasil karakterisasi FTIR tidak menunjukkan terjadinya perubahan yang signifikan terhadap gugus fungsi TiO2/zeolit setelah pemakaian dan sebelum pemakaian. Pada pola XRD dapat diamati bahwa katalis TiO2/zeolit telah berhasil terbentuk ditandai dengan munculnya puncak tertinggi pada 2 θ = 24.9500 yang menandai puncak anatase dan 26.5940 yang menunjukkan puncak dari SiO2.Dari hasil persentase yang didapatkan 20 g TiO2/zeolit telah dapat mendegradasi Congo Red 20 mg/L dibawah sinar lampu UV 365 nm selama 60 menit hingga 94,23 % dan simulasi limbah Congo Red hingga 85,14 %. Kata Kunci : TiO2/zeolit, Congo Red, Simulasi Limbah Congo Red, Fotokatalis ABSTRACT UTILIZATION NATURAL ZEOLITE FROM WEST SUMATERA FOR TiO2 SUPPORT IN DEGRADATION OF CONGO RED AND A WASTE SIMULATION BY PHOTOLYSIS By : Muhammad Lucky Fajri (1210413030) Dr. Zilfa, M.S dan Rahmayeni, M.S Zeolite Clinoptilolite-Ca was succesfully supported TiO2 in synthesis TiO2/zeolite as photocatalyst in degradation of Congo Red 20 mg/L and a waste simulation of Congo Red under UV light irradiation 365 nm. TiO2/zeolite were characterized by Fourier Transform Infra Red (FTIR) and X-Ray Diffraction (XRD). The result of FTIR showed the structure fungsional of TiO2/zeolit not change before and after degradation. The XRD patterns showed TiO2/zeolite photocatalyst were succesfully formed, it proved with the highest peaks at 2 θ = 24.9500 , which were corresponded to anatase peaks and 26.5940 to SiO2 peaks. The persentage degradation showed 20 g TiO2/zeolite degradated Congo Red 20 mg/L under UV light irradiation 365 nm with 60 minute reached 94,23 % and a waste simulation of Congo Red reached 85,14 %. Key Word: TiO2/zeolite, Photocatalyst, Congo Red, A Waste simulation of Congo Red