DEGRADASI ZAT WARNA KATIONIK DAN ANIONIK MENGGUNAKAN IMMOBILISASI FOTOKATALIS TIO2/?-FE2O3/BENTONIT DI BAWAH LAMPU FLUORESCENCE
| Main Author: | FERIZKA FRASTIWI |
|---|---|
| Format: | |
| Terbitan: |
Fakultas mipa
, 2018
|
| Online Access: |
http://etd.unsyiah.ac.id//index.php?p=show_detail&id=50169 |
Daftar Isi:
- ABSTRAKImmobilisasi TiO2/Fe2O3/Bentonit telah dilakukan menggunakan metode Brush coating dengan double sided adhesive tape (DSAT) sebagai perekatnya. Formulasi komposit TiO2/Fe2O3/Bentonit terimmobilisasi dibuat dengan mencampurkan aquadest kedalam TiO2 P25, Fe2O3 dan Bentonit dengan perbandingan massa (g) 4 : 0,25 : 1. Aktivitas fotokatalitik fotokatalis terimmobilisasi dievaluasi menggunakan zat warna methylene blue (MB) dan indigo carmine (IC). Bentonit dan hematite dikarakterisasi menggunakan XRD. Morfologi permukaan dari hematit (?-Fe2O3) dan komposit TiO2/?-Fe2O3/Bentonit dikarterisasi menggunakan SEM. Hasil penelitian menunjukkan bahwa aktivitas fotokatalitik yang optimum dalam mendegradasi zat warna IC yaitu pada massa komposit sebesar 60 mg, pH 5 dan konsentrasi 25 ppm dengan degradasi (%) sebesar 97,2%, sedangkan untuk zat warna MB diperoleh degradasi (%) sebesar 98,6% dengan keadaan optimumnya pada massa fotokatalis sebesar 60 mg, pH awal larutan zat warna yaitu pH 6 dan konsentrasi 25 ppm pada waktu radiasi 60 menit. Regenerasi komposit TiO2/?-Fe2O3/Bentonit terhadap zat warna MB dan IC dilakukan sebanyak 5 kali dengan aktivitas fotokatalitiknya yang hampir sama yaitu sebesar 98,62 %, 98,59%, 98,59%, 98,59%, 98,59% untuk zat warna MB dan 97,19%, 97,80%, 97,08 %, 97,08% untuk zat warna IC berturut turut. Kata kunci : fotokatalis, zat warna kationik, zat warna anionik, immobilisasi, TiO2, ?-Fe2O3, Bentonit?ABSTRACTImmobilization of TiO2/?-Fe2O3/Bentonit was carried out using the Brush coating method and double sided adhesive tape as a binder. Formulation of immobilized TiO2/?-Fe2O3/Bentonit composite was made by mixing aquadest into TiO2 P25, Fe2O3 and Bentonite with mass ratio (g) of 4 : 0.25 : 1. Photocatalytic activity of immobilized photocatalysts was evaluated using methylene blue (MB) and indigo carmine (IC) dyes. Bentonite and hematite are characterized using XRD. Surface morphology of hematite (?-Fe2O3) and TiO2/?-Fe2O3/Bentonit composites were chartered using SEM. The results showed that the optimum photocatalytic activity in the degradation of IC dyes were at the composite mass of 60 mg, pH 5 and concentration of 25 ppm with degradation (%) of 97.2%, while in MB dyes obtained degradation (%) was 98.6% with the optimum conditions were on photocatalyst mass of 60 mg, initial pH of the dye at pH 6 and concentration of solution 25 ppm with 60 minutes of irradiation time. Regeneration of TiO2/?-Fe2O3/Bentonit composites for degradation MB dyes and IC was carried out 5 cycles which gave similar photocatalytic activity results were 98.62%, 98.59%, 98.59%, 98.59%, 98.59% for MB dyes solution and 97.19%, 97.80%, 97.08%, 97.08% for IC dyes solutions respectively. Key word : photocatalysts, cationic dye, anionic dye,immobilization, TiO2, ?-Fe2O3, Bentonit
- Banda Aceh