Characterization Of Modified Bentonite Using Aluminum Polycation = Karakterisasi Bentonit Termodifikasi dengan Polikation Aluminium
| Main Author: | Perpustakaan UGM, i-lib |
|---|---|
| Format: | Article NonPeerReviewed |
| Terbitan: |
[Yogyakarta] : Universitas Gadjah Mada
, 2002
|
| Subjects: | |
| Online Access: |
https://repository.ugm.ac.id/17853/ http://i-lib.ugm.ac.id/jurnal/download.php?dataId=621 |
Daftar Isi:
- ABSTRACT The modification of bentonite by pillarization using aluminum polycation type Keggin [Al 1304(OH)24(H20)1217+ has been carried out, by exchange of cation from interlayer with aluminum polycation. The amount of aluminum polycation, which was used for the pillaring of bentonite was varied, i.e. 5 mmol/gram, 10 mmol/gram, and 20 mmol/gram of bentonite. After drying, the pillared bentonite was calcined at 400 °C for 6 hour with temperature rate of 5 °C/min. The cationic exchange capacity (CEC) of starting bentonite was 98.3 meq/100 gram. The concentration ratio of Al/Si increased from 0.27 to 0.34 for pillared bentonite and of Ca/Si was decreased from 0.06 to 0.006 for pillared bentonite. The basal space for pillared bentonit increased significantly from 7.30 A to about 18 A . The measured specific surface area (by BET) of pillared bentonite was also increased significantly from 46 m2/g to about 162 m2/g. It was concluded that bentonite has been pillared by aluminum polication successfully. Keywords: aluminum polycation, bentonite