Pengaruh Temperatur Sintering Terhadap Sifat Fisis Dan Sifat Mekanis Kopling Plat Gesek
| Main Author: | Widhiarta, Indra |
|---|---|
| Format: | Karya Ilmiah NonPeerReviewed application/pdf |
| Bahasa: | eng |
| Terbitan: |
, 2012
|
| Subjects: | |
| Online Access: |
http://eprints.ums.ac.id/20194/1/03._Halaman_Depan.pdf http://eprints.ums.ac.id/20194/2/04._BAB_I.pdf http://eprints.ums.ac.id/20194/4/05._BAB_II.pdf http://eprints.ums.ac.id/20194/5/06._BAB_III.pdf http://eprints.ums.ac.id/20194/12/07._BAB_IV.pdf http://eprints.ums.ac.id/20194/13/08._BAB_V.pdf http://eprints.ums.ac.id/20194/15/09._DAFTAR_PUSTAKA.pdf http://eprints.ums.ac.id/20194/20/10._Lampiran.pdf http://eprints.ums.ac.id/20194/23/02._Naskah_Publikasi.pdf http://eprints.ums.ac.id/20194/ |
| ctrlnum |
20194 |
|---|---|
| fullrecord |
<?xml version="1.0"?>
<dc schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd"><relation>http://eprints.ums.ac.id/20194/</relation><title>Pengaruh Temperatur Sintering Terhadap Sifat Fisis Dan Sifat
Mekanis Kopling Plat Gesek

</title><creator>Widhiarta, Indra </creator><subject>T Technology (General)</subject><description>Perkembangan dan penggunaan kampas selama ini semakin berkembang
pesat dan semakin banyak jenisnya sehingga penelitian ini bertujuan untuk
membuat suatu bahan komposit yang berfungsi untuk kampas kopling dengan
beberapa jenis bahan yang aman bagi kesehatan dan dengan suhu sintering
yang berbeda dengan menggunakan teknologi serbuk.
Bahan yang digunakan dalam penelitian ini adalah serbuk 30%
aluminium, 30% serbuk tembaga, 20% serat kelapa yang telah disaring dan
20% resin polyester dengan katalis sebagai pengikatnya. Bahan ini dicampur
kemudian dipress dengan beban 3 ton selama 60 menit, kemudian di sintering
dengan suhu 180° C,205° C, dan 230° C selama 40 menit .Untuk proses
pengujian yaitu pengujian kekerasan dengan metode brinell untuk mengetahui
tingkat kekerasan dan pengujian keausan dengan mesin yang tersedia dibengkel
yang berfungsi untuk mengetahui besar keausan.
Dari data hasil penelitian uji kekerasan di peroleh kekerasan yang paling
besar yaitu pada suhu sintering 180° C dengan nilai kekerasan 8,698 HB dan
nilai kekerasan terendah pada suhu sintering 230° C dengan nilai kekerasan
6,250 HB. Selain itu peningkatan suhu sintering juga berpengaruh terjadi
peningkatan nilai keausan walaupun tidak terlalu signifikan. Nilai keausan
terendah pada suhu sintering 180° C yaitu (uji kering 0,55 mm dengan koefisien
gesek 0,280), (uji oil 0,07 mm dengan koefisien gesek 0,272) dan nilai keausan
tertinggi pada suhu sintering 230° C dengan nilai keausan (uji kering 0,59 mm
.dengan koefisien gesek 0,270), (uji oil 0,11 mm dengan koefisien gesek 0,272)</description><date>2012</date><type>Other:Karya Ilmiah</type><type>PeerReview:NonPeerReviewed</type><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/1/03._Halaman_Depan.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/2/04._BAB_I.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/4/05._BAB_II.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/5/06._BAB_III.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/12/07._BAB_IV.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/13/08._BAB_V.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/15/09._DAFTAR_PUSTAKA.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/20/10._Lampiran.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20194/23/02._Naskah_Publikasi.pdf</identifier><identifier> Widhiarta, Indra (2012) Pengaruh Temperatur Sintering Terhadap Sifat Fisis Dan Sifat Mekanis Kopling Plat Gesek. Skripsi thesis, Universitas Muhammadiyah Surakarta. </identifier><relation>D200050124</relation><recordID>20194</recordID></dc>
|
| language |
eng |
| format |
Other:Karya Ilmiah Other PeerReview:NonPeerReviewed PeerReview File:application/pdf File |
| author |
Widhiarta, Indra |
| title |
Pengaruh Temperatur Sintering Terhadap Sifat Fisis Dan Sifat
Mekanis Kopling Plat Gesek |
| publishDate |
2012 |
| topic |
T Technology (General) |
| url |
http://eprints.ums.ac.id/20194/1/03._Halaman_Depan.pdf http://eprints.ums.ac.id/20194/2/04._BAB_I.pdf http://eprints.ums.ac.id/20194/4/05._BAB_II.pdf http://eprints.ums.ac.id/20194/5/06._BAB_III.pdf http://eprints.ums.ac.id/20194/12/07._BAB_IV.pdf http://eprints.ums.ac.id/20194/13/08._BAB_V.pdf http://eprints.ums.ac.id/20194/15/09._DAFTAR_PUSTAKA.pdf http://eprints.ums.ac.id/20194/20/10._Lampiran.pdf http://eprints.ums.ac.id/20194/23/02._Naskah_Publikasi.pdf http://eprints.ums.ac.id/20194/ |
| contents |
Perkembangan dan penggunaan kampas selama ini semakin berkembang
pesat dan semakin banyak jenisnya sehingga penelitian ini bertujuan untuk
membuat suatu bahan komposit yang berfungsi untuk kampas kopling dengan
beberapa jenis bahan yang aman bagi kesehatan dan dengan suhu sintering
yang berbeda dengan menggunakan teknologi serbuk.
Bahan yang digunakan dalam penelitian ini adalah serbuk 30%
aluminium, 30% serbuk tembaga, 20% serat kelapa yang telah disaring dan
20% resin polyester dengan katalis sebagai pengikatnya. Bahan ini dicampur
kemudian dipress dengan beban 3 ton selama 60 menit, kemudian di sintering
dengan suhu 180° C,205° C, dan 230° C selama 40 menit .Untuk proses
pengujian yaitu pengujian kekerasan dengan metode brinell untuk mengetahui
tingkat kekerasan dan pengujian keausan dengan mesin yang tersedia dibengkel
yang berfungsi untuk mengetahui besar keausan.
Dari data hasil penelitian uji kekerasan di peroleh kekerasan yang paling
besar yaitu pada suhu sintering 180° C dengan nilai kekerasan 8,698 HB dan
nilai kekerasan terendah pada suhu sintering 230° C dengan nilai kekerasan
6,250 HB. Selain itu peningkatan suhu sintering juga berpengaruh terjadi
peningkatan nilai keausan walaupun tidak terlalu signifikan. Nilai keausan
terendah pada suhu sintering 180° C yaitu (uji kering 0,55 mm dengan koefisien
gesek 0,280), (uji oil 0,07 mm dengan koefisien gesek 0,272) dan nilai keausan
tertinggi pada suhu sintering 230° C dengan nilai keausan (uji kering 0,59 mm
.dengan koefisien gesek 0,270), (uji oil 0,11 mm dengan koefisien gesek 0,272) |
| id |
IOS2728.20194 |
| institution |
Universitas Muhammadiyah Surakarta |
| institution_id |
249 |
| institution_type |
library:university library |
| library |
Perpustakaan Universitas Muhammadiyah Surakarta |
| library_id |
555 |
| collection |
Digital Repository Universitas Muhammadiyah Surakarta |
| repository_id |
2728 |
| subject_area |
Agama Ekonomi Farmasi |
| city |
KOTA SURAKARTA |
| province |
JAWA TENGAH |
| repoId |
IOS2728 |
| first_indexed |
2016-09-22T02:43:30Z |
| last_indexed |
2016-09-22T02:43:31Z |
| recordtype |
dc |
| _version_ |
1765810726226624512 |
| score |
17.538404 |