Pengaruh Perlakuan Pendinginan Pada Proses Pengelasan Smaw(Shielded Metal Arc Welding) Stainless Steel Austenitik Aisi 201 Terhadap Uji Komposisi Kimia, Uji Struktur Mikro, Uji Kekerasan Dan Uji Tarik
| Main Author: | BUDIANTO, ARI |
|---|---|
| Format: | Karya Ilmiah NonPeerReviewed application/pdf |
| Bahasa: | eng |
| Terbitan: |
, 2012
|
| Subjects: | |
| Online Access: |
http://eprints.ums.ac.id/20101/1/03._Halaman_Depan.pdf http://eprints.ums.ac.id/20101/2/04._BAB_I.pdf http://eprints.ums.ac.id/20101/5/05._BAB_II.pdf http://eprints.ums.ac.id/20101/6/06._BAB_III.pdf http://eprints.ums.ac.id/20101/8/07._BAB_IV.pdf http://eprints.ums.ac.id/20101/9/08._BAB_V.pdf http://eprints.ums.ac.id/20101/11/09._Daftar_Pustaka.pdf http://eprints.ums.ac.id/20101/12/10._Lampiran.pdf http://eprints.ums.ac.id/20101/14/02._Naskah_Publikasi.pdf http://eprints.ums.ac.id/20101/ |
| ctrlnum |
20101 |
|---|---|
| fullrecord |
<?xml version="1.0"?>
<dc schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/ http://www.openarchives.org/OAI/2.0/oai_dc.xsd"><relation>http://eprints.ums.ac.id/20101/</relation><title>Pengaruh Perlakuan Pendinginan Pada Proses Pengelasan Smaw(Shielded Metal Arc Welding) Stainless Steel Austenitik Aisi 201 Terhadap Uji Komposisi Kimia, Uji Struktur Mikro, Uji Kekerasan Dan Uji Tarik
</title><creator>BUDIANTO, ARI </creator><subject>TJ Mechanical engineering and machinery</subject><description>Tujuan dari penelitian ini adalah untuk mengetahui perubahan struktur
mikro dan sifat mekanis pada baja karbon AISI 201 setelah mendapat
pengelasan khususnya pada daerah las, has dan logam induk. Pengelasan
dilakukan dengan menggunakan proses SMAW (Shielded Metal Arc Welding
) dan dilakukan variasi pendinginan yaitu dengan udara dan air.
Bahan uji adalah baja tahan karat stainless steel 201 dengan metode
pengujian yang dilakukan adalah : uji kompoisi kimia, uji struktur mikro, uji
kekerasan dan uji tarik
Dari hasil uji komposisi kimia didapatkan hasil pengujian sebagai
berikut : besi (Fe) = 71,1 %, mangan (Mn) = 16,0 %, Chrom (Cr) = 11,3 %,
Nikel (Ni) = 0,527 %, untuk unsur tambahan lainnya didapatkan prosentase
dalam jumlah kecil yaitu kurang dari 0,05 %, unsur unsur tersebut adalah
Silisium(Si), Niobdenum (Nb) , Titanium (Ti), Alumunium (Al) , Wolfram (W) ,
Plumbum (Pb), Phospor (P), Sulfur (S), Molibdenum (Mo). Pada
pengamatan struktur mikro pendinginan air pada daerah logam induk
didapatkan bahwa struktur karbida chrom memiliki jumlah lebih banyak dan
tersebar disemua bagian dibanding dengan pendinginan udara,pada daerah
las pendinginan dengan air dan udara didapatkan bahwa struktur nikel dan
austenite lebih dominan, sedangkan pada daerah haz baik pendinginan air
dan udara struktur khrom dan karbida chrom mulai tampak.Dari uji kekerasan
didapatkan bahwa harga kekerasan terendah pada daerah las dengan
pendinginan udara yaitu 182,9 VHN,dan kekerasan tertinggi yaitu 241,8
VHN. Sedangkan pada uji tarik tegangan rata-rata tertinggi yaitu 70,43
kg/mm2 pada pendinginan udara.
</description><date>2012</date><type>Other:Karya Ilmiah</type><type>PeerReview:NonPeerReviewed</type><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/1/03._Halaman_Depan.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/2/04._BAB_I.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/5/05._BAB_II.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/6/06._BAB_III.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/8/07._BAB_IV.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/9/08._BAB_V.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/11/09._Daftar_Pustaka.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/12/10._Lampiran.pdf</identifier><type>File:application/pdf</type><language>eng</language><identifier>http://eprints.ums.ac.id/20101/14/02._Naskah_Publikasi.pdf</identifier><identifier> BUDIANTO, ARI (2012) Pengaruh Perlakuan Pendinginan Pada Proses Pengelasan Smaw(Shielded Metal Arc Welding) Stainless Steel Austenitik Aisi 201 Terhadap Uji Komposisi Kimia, Uji Struktur Mikro, Uji Kekerasan Dan Uji Tarik. Skripsi thesis, Universitas Muhammadiyah Surakarta. </identifier><relation>D200040054</relation><recordID>20101</recordID></dc>
|
| language |
eng |
| format |
Other:Karya Ilmiah Other PeerReview:NonPeerReviewed PeerReview File:application/pdf File |
| author |
BUDIANTO, ARI |
| title |
Pengaruh Perlakuan Pendinginan Pada Proses Pengelasan Smaw(Shielded Metal Arc Welding) Stainless Steel Austenitik Aisi 201 Terhadap Uji Komposisi Kimia, Uji Struktur Mikro, Uji Kekerasan Dan Uji Tarik |
| publishDate |
2012 |
| topic |
TJ Mechanical engineering and machinery |
| url |
http://eprints.ums.ac.id/20101/1/03._Halaman_Depan.pdf http://eprints.ums.ac.id/20101/2/04._BAB_I.pdf http://eprints.ums.ac.id/20101/5/05._BAB_II.pdf http://eprints.ums.ac.id/20101/6/06._BAB_III.pdf http://eprints.ums.ac.id/20101/8/07._BAB_IV.pdf http://eprints.ums.ac.id/20101/9/08._BAB_V.pdf http://eprints.ums.ac.id/20101/11/09._Daftar_Pustaka.pdf http://eprints.ums.ac.id/20101/12/10._Lampiran.pdf http://eprints.ums.ac.id/20101/14/02._Naskah_Publikasi.pdf http://eprints.ums.ac.id/20101/ |
| contents |
Tujuan dari penelitian ini adalah untuk mengetahui perubahan struktur
mikro dan sifat mekanis pada baja karbon AISI 201 setelah mendapat
pengelasan khususnya pada daerah las, has dan logam induk. Pengelasan
dilakukan dengan menggunakan proses SMAW (Shielded Metal Arc Welding
) dan dilakukan variasi pendinginan yaitu dengan udara dan air.
Bahan uji adalah baja tahan karat stainless steel 201 dengan metode
pengujian yang dilakukan adalah : uji kompoisi kimia, uji struktur mikro, uji
kekerasan dan uji tarik
Dari hasil uji komposisi kimia didapatkan hasil pengujian sebagai
berikut : besi (Fe) = 71,1 %, mangan (Mn) = 16,0 %, Chrom (Cr) = 11,3 %,
Nikel (Ni) = 0,527 %, untuk unsur tambahan lainnya didapatkan prosentase
dalam jumlah kecil yaitu kurang dari 0,05 %, unsur unsur tersebut adalah
Silisium(Si), Niobdenum (Nb) , Titanium (Ti), Alumunium (Al) , Wolfram (W) ,
Plumbum (Pb), Phospor (P), Sulfur (S), Molibdenum (Mo). Pada
pengamatan struktur mikro pendinginan air pada daerah logam induk
didapatkan bahwa struktur karbida chrom memiliki jumlah lebih banyak dan
tersebar disemua bagian dibanding dengan pendinginan udara,pada daerah
las pendinginan dengan air dan udara didapatkan bahwa struktur nikel dan
austenite lebih dominan, sedangkan pada daerah haz baik pendinginan air
dan udara struktur khrom dan karbida chrom mulai tampak.Dari uji kekerasan
didapatkan bahwa harga kekerasan terendah pada daerah las dengan
pendinginan udara yaitu 182,9 VHN,dan kekerasan tertinggi yaitu 241,8
VHN. Sedangkan pada uji tarik tegangan rata-rata tertinggi yaitu 70,43
kg/mm2 pada pendinginan udara.
|
| id |
IOS2728.20101 |
| institution |
Universitas Muhammadiyah Surakarta |
| institution_id |
249 |
| institution_type |
library:university library |
| library |
Perpustakaan Universitas Muhammadiyah Surakarta |
| library_id |
555 |
| collection |
Digital Repository Universitas Muhammadiyah Surakarta |
| repository_id |
2728 |
| subject_area |
Agama Ekonomi Farmasi |
| city |
KOTA SURAKARTA |
| province |
JAWA TENGAH |
| repoId |
IOS2728 |
| first_indexed |
2016-09-22T02:43:26Z |
| last_indexed |
2016-09-22T02:43:26Z |
| recordtype |
dc |
| _version_ |
1765810725621596160 |
| score |
17.538404 |