PEMANFAATAN KOMPOSIT KITOSAN ZnO-SiO2 SEBAGAI AGEN ANTIBAKTERITERHADAP BAKTERI Staphylococcus aureus PADA KAIN KATUNTHE USE OF CHITOSAN ZnO-SiO2 COMPOSITE AS ANTIBACTERIAL AGENT OFStaphylococcus aureus BACTERIA IN COTTON FABRIC
| Main Author: | SETIYANI, RIRIN |
|---|---|
| Format: | eJournal |
| Bahasa: | ind |
| Terbitan: |
UNESA Journal of Chemistry
, 2015
|
| Online Access: |
http://ejournal.unesa.ac.id/index.php/unesa-journal-of-chemistry/article/view/12285 |
Daftar Isi:
- Abstrak. Telah dilakukan penelitian tentang pembuatan dan karakterisasi komposit kitosan ZnO-SiO2sebagai agen antibakteri yang diaplikasikan pada kain katun dengan metode pelapisan pencelupan atau dipcoatingdan dengan teknik pengeringan pad dry-cure. Penelitian ini bertujuan untuk mendapatkan dataaktivitas antibakteri kain katun terlapisi komposit kitosan ZnO-SiO2 yang memberikan nilai aktivitasantibakteri terhadap bakteri Staphylococcus aureus yang paling tinggi. Komposit kitosan ZnO-SiO2 dibuatdengan perbandingan % volum 1:0,5:1; 1:1:1 dan 1:1,5:1 yang hasilnya akan dianalisis menggunakanspektrofotometer FTIR. Hasil analisis FTIR menunjukkan bahwa telah terjadi interaksi antara kitosandengan sol ZnO-SiO2 pada pita serapan 3433 cm-1 sampai 3448,72 cm-1, dan terjadi pergeseran bilangangelombang kitosan dengan sol ZnO-SiO2 pada pita serapan 1635,64 cm-1 sampai 1566,20 cm-1. Terdapatserapan khas vibrasi Si-O-Zn pada daerah bilangan gelombang 1411,89cm-1. Terdapat pita serapan yang khasvibrasi Zn-O dan N-Zn pada daerah bilangan gelombang 462,92 cm-1, 570,93 cm-1,617,22 cm-1, 671,23 cm-1menandakan bahwa Zn terintegrasi pada komposit. Aktivitas antibakteri kain terlapisi kitosan ZnO-SiO2dengan perbandingan komposisi 1:1,5:1 memiliki aktivitas antibakteri tersebsar yaitu sebesar 89,042 %.Kata kunci: agen antibakteri, kitosan, , komposit, silika,.Abstract. The experiment of synthesis and characterization of chitosan ZnO-SiO2 composite as antibacterialagent which applied to cotton fabric by dip coating method and drying techniques pad dry-cure have beenconducted. Purpose of this experiment was to gain the data of antibacterial activity of cotton fabric coatedwith chitosan ZnO-SiO2 composite which give the highest antibacterial activity to chitosan ZnO-SiO2composite. Chitosan ZnO-SiO2 composite composition was made with ratio % volume 1:0,5:1; 1:1:1; and1:1,5:1 which the result will be analyzed by FTIR Spectrophotometer. The result of FTIR analysis shows thatthere was decreasing interaction between chitosan and ZnO-SiO2 sol in absorption band 3433 cm-1 to3433,72 cm-1, and there was movement of chitosan wave number in adsorption band 1635,64 cm-1 to 1566,20cm-1. There was special absorption band of Si-O-Zn vibration in wave number area 1411,89cm-1. There wasspecial absorption band of Zn-O and N-Zn vibration in wave number area of 462,92 cm-1 , 570,93 cm-1;617,22 cm-1 dan 671,23 cm-1. It shows that Zn can be integrated to composite. Antibacterial activity of fabriccoated with chitosan ZnO-SiO2 composite with composition ratio 1:1,5:1 was 89,042%Key words: antibacterial agent, chitosan , composite , silica