BIODEGRADABLE PLASTICS FROM A MIXTURE OF LOW DENSITY POLYETHYLENE (LDPE) AND CASSAVA STARCH WITH THE ADDITION OF ACRYLIC ACID
| Main Authors: | Susilawati, Susilawati, Mustafa, Irfan, Maulina, Desy |
|---|---|
| Format: | Article info application/pdf eJournal |
| Bahasa: | eng |
| Terbitan: |
Syiah Kuala University
, 2013
|
| Online Access: |
http://www.jurnal.unsyiah.ac.id/natural/article/view/578 http://www.jurnal.unsyiah.ac.id/natural/article/view/578/488 |
Daftar Isi:
- A research of preparation biodegradable plastics, from LDPE and cassava starch mixture with the addition of acrylic acid, had been conducted. This research purpose to studied compatibility properties of the material and percent weight loss during the biodegradation test. Optimum weight loss (59,26% ) was showed after 60 days witches LDPE and starch composition ratio 6 : 4 (w/w) while tensile strength equal to 0,38 Kgf/mm2. SEM characterization showed that biodegradation has occurred by formation of hole in the biodegradable plastic surface. DTA test gave Tg = 130 °C, Tm = 230 °C and Td = 370-450 °C while FT-IR analysis showed that the biodegradable plastics have a chemistry interaction.