Failure Analysis of Motorbike Brake Disc Due To Thermal Loading Review
| Main Authors: | Mr.Avinash G. Patil, Mr. Bhuhan N.Ghodake, Mr. Ganesh G. Patil |
|---|---|
| Format: | Article Journal |
| Bahasa: | eng |
| Terbitan: |
, 2019
|
| Subjects: | |
| Online Access: |
https://zenodo.org/record/2621107 |
Daftar Isi:
- Fatigue fracture is the fundamental reason for failure of engineering components it is cause by growth of initial crack and its propagation at micro structural level under thermal cyclic loading. A complex combination of thermo –mechanical loading subjected to component for crack initiation and growth by thermal fatigue. A certain number of motorbike disc shown the presence of small crack only after few thousand miles. This study focus on the evaluation of a surface crack in a stainless steel specimen expose to thermo-mechanical loading inducing a thermal gradient in the thickness. The thermo- mechanical modal is proposed in this study having initial crack under mode-I under thermal cyclic loading both in plane stress and in plane strain condition. A FEM analysis was performed to determine the temperature & stress distribution in disc during braking. Experimental facilities used for generating heating and cooling cycle.