Mesoporous Material Nanofibers by Electrospinning
| Main Authors: | Sh. Sohrabnezhad, A. Jafarzadeh |
|---|---|
| Format: | Article |
| Bahasa: | eng |
| Terbitan: |
, 2016
|
| Subjects: | |
| Online Access: |
https://zenodo.org/record/1125939 |
Daftar Isi:
- In this paper, MCM-41 mesoporous material nanofibers were synthesized by an electrospinning technique. The nanofibers were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), x-ray diffraction (XRD), and nitrogen adsorption–desorption measurement. Tetraethyl orthosilicate (TEOS) and polyvinyl alcohol (PVA) were used as a silica source and fiber forming source, respectively. TEM and SEM images showed synthesis of MCM-41 nanofibers with a diameter of 200 nm. The pore diameter and surface area of calcined MCM-41 nanofibers was 2.2 nm and 970 m2/g, respectively. The morphology of the MCM-41 nanofibers depended on spinning voltages.